Iya aiki (Ml) |
Jigilar kwalban (mm) |
Jigilar kwalban ciki (mm) |
Kwalban kwalba diamita (mm) |
Tsawo (mm) |
Dutsen zinariya |
Abu |
Launi |
|
1000 |
99 |
30 |
40 |
230 |
45 |
Gilashin borosilics |
Share \ / Brown |


|
Sio2 abun ciki |
> 80% |
|
Iri aya |
520℃ |
|
Annealing Point |
560℃ |
|
Mai laushi |
820℃ |
|
Ganyayyaki mai daɗi |
1.47 |
|
Haske Watsawa (2mm) |
0.92 |
|
Modulus na roba |
67KNM-2 |
|
Da tenerile |
40-120nm-2 |
|
Gilashin damuwa na gilashi |
3.8 * 10-6mm2 \ / n |
|
Aiki zazzabi (104DPAS) |
1220℃ |
|
Linear da aka samu na fadada (20-300℃) |
3.3 * 10-6k-1 |
|
Yawa (20℃) |
2.23GCM-1 |
|
Takamaiman zafi |
0.9jg-1k-1 |
|
A halin da ake yi na thereral |
1.2wm-1k-1 |
|
HydrolyTic resistance (ISO 719) |
Sa 1 |
|
Acid juriya (ISO 715) |
Sa 1 |
|
Alkali resistance (ISO 695) |
Sa 2 |
|
Jerwararrakin shukar jiki (ISO 715) Rod 6 * 30mm |
300℃ |